Flexural strength and Vickers hardness of milled and 3D-printed resins for provisional dental restorations

Various forms of temporary resins are offered on the market; however, the properties of temporary resins obtained by milling and 3D printing have not been fully examined. This study aimed to compare the flexural strength and Vickers hardness of milled and 3D-printed resins. Methods: Three resins were tested: Evolux PMMA (milled resin), Cosmos Temp (3D-printed resin), and Structur 2 SC (bis-acrylic resin, group control). Specimens were prepared with rectangular shapes (n = 12) for flexural strength measurements and disc shapes (n = 9) for Vickers hardness tests. Flexural strength tests were performed at a crosshead speed of 0.75 mm/min, and the Vickers hardness was measured under a load of 20 N for 10 s. The obtained data were subjected to the Kruskal­Wallis test. Results: A significant difference (p < 0.05) in flexural strength was observed among the three sample groups: Evolux PMMA (111.76 MPa), Structur 2 SC (87.34 MPa), and Cosmos Temp (56.83 MPa). No significant difference (p < 0.05) was observed between the Vickers hardness values of Structur 2 SC (33.37 VHN) and Evolux PMMA (29.11 VHN); however, both materials were statistically superior to Cosmos Temp (10.90 VHN). Conclusion: While the mechanical properties of the milled resin were superior or similar to those of the bisacrylic resin, the 3D-printed resin was statistically inferior to both the milled and bis-acrylic resins

Influence of fluoride-releasing materials in the inhibition of enamel and dentin demineralization around restorations / Influência de materiais liberadores de flúor na inibição da desmineralização do esmalte e da dentina ao redor de restaurações

Objective: The aim was to evaluate the influence of fluoride-releasing restorative materials in enamel and dentin microhardness. Material and Methods: 40 blocks (5x5x3 mm) from cervical third of human molars received a cavity preparation between the enamel and dentin, and the restorations were subjected to in vitro caries model. Specimens were randomly restored with (n=10): conventional glass ionomer cement (Ketac Cem, 3M ESPE); polyacid-modified composite resin (Ionoseal, VOCO); resin-modified glass ionomer cement (Ionofast, Biodinâmica); or microhybrid composite resin (Filtek Z250, 3M ESPE). The specimens were sectioned longitudinally and enamel and dentin Knoop microhardness were determined at different distances from the restorative material (100, 200 and 300 µm) and depth of surface (20, 40 and 60 µm). The data were submitted to three-way repeated measures ANOVA and Tukey ́s test ( α =0.05). Results: For enamel, the double interactions between material x distance and material x depth were statistically significant. In all depths and distances, the highest values of enamel microhardness were observed for Ketac Cem. In dentin, the materials differed statistically from each other, and Ionoseal obtained higher microhardness values than those found in Ionofast. Conclusion: Conventional glass ionomer cement is more effective in preventing enamel demineralization around restoration followed by the polyacid-modified composite resin. In dentin, the polyacid-modified composite resin obtained better performance than resin-modified glass ionomer cement. (AU)

Objetivo: O objetivo foi avaliar a influência de materiais restauradores liberadores de flúor na microdureza do esmalte e da dentina. Material e Métodos: 40 blocos (5x5x3 mm) do terço cervical de molares humanos receberam preparo cavitário entre esmalte e dentina, e após a restauração foram submetidas a um modelo in vitro de cárie. As amostras foram restauradas aleatoriamente com (n=10): cimento de ionômero de vidro convencional (Ketac Cem, 3M ESPE); resina composta modificada por poliácidos (Ionoseal, VOCO); cimento de ionômero de vidro modificado por resina (Ionofast, Biodinâmica); ou resina composta microhíbrida (Filtek Z250, 3M ESPE). As amostras foram seccionadas longitudinalmente e a microdureza Knoop de esmalte e dentina foi determinada em diferentes distâncias do material restaurador (100, 200 e 300 µm) e profundidade de superfície (20, 40 e 60 µm). Os dados foram submetidos à ANOVA para medidas repetidas de três fatores e teste de Tukey (α =0,05). Resultados: Para o esmalte, as duplas interações entre material x distância e material x profundidade foram estatisticamente significativas. Em todas as profundidades e distâncias, os maiores valores de microdureza do esmalte foram observados para o Ketac Cem. Na dentina, Ionoseal obteve valores de microdureza superiores aos encontrados no Ionofast. Conclusão:O cimento de ionômero de vidro convencional é mais eficaz na prevenção da desmineralização do esmalte ao redor da restauração, seguido pela resina composta modificada por poliácidos. Na dentina, a resina composta modificada por poliácidos obteve melhor desempenho que o cimento de ionômero de vidro modificado por resina. (AU)

Influence of calcium lactate and sodium fluoride solution mouthwashes on enamel microhardness and dentin permeability during in-office bleaching / Influência das soluções enxaguatórias de lactato de cálcio e fluoreto de sódio na microdureza do esmalte e permeabilidade dentinária durante o clareamento em consultório

Objective: This study evaluated the influence of calcium lactate and sodium fluoride mouthwashes on enamel microhardness and dentin permeability during in-office bleaching. Material and Methods: For the microhardness evaluation, enamel blocks were randomly submitted to different treatments associated with in-office bleaching agent using 40% hydrogen peroxide (Opalescence Boost PF 40%/ Ultradent; 3 sessions x 40-minute each) (n = 10): 1) Control: application of bleaching agent; 2) Calcium lactate: 1-minute immersion before bleaching treatment; 3) Sodium fluoride: immersion for 1 minute before bleaching treatment; 4) Calcium lactate + sodium fluoride: 1 minute immersion in calcium lactate solution, followed by 1 minute immersion in sodium fluoride before bleaching treatment. Dentin discs received the same treatment protocols (n = 10) to evaluate permeability. Knoop microhardness and dentin permeability assessments were performed twice (at baseline and 48 hours after the end of bleaching treatment). Results: The generalized linear model considering the design of repeated measures over time showed that there was no significant difference between treatments (p = 0.9577) and between assessments (p = 0.3267) regarding Knoop microhardness. Kruskal Wallis and Dunn tests showed that calcium lactate immersion before bleaching treatment provided higher dentin permeability than other groups (p = 0.0009). Conclusion: The use of sodium fluoride solution and calcium lactate in association with in-office bleaching treatment did not influence the microhardness of tooth enamel, although calcium lactate may increase dentin permeability. (AU)

Objetivo: Este estudo avaliou a influência dos enxaguatórios bucais com lactato de cálcio e fluoreto de sódio na microdureza do esmalte e na permeabilidade da dentina durante o clareamento em consultório. Material e Métodos: Para avaliação da microdureza, blocos de esmalte foram submetidos aleatoriamente a diferentes tratamentos associados a agente clareador em consultório com peróxido de hidrogênio 40% (Opalescence Boost PF 40% / Ultradent; 3 sessões x 40 minutos cada) (n = 10): 1) Controle: aplicação de agente clareador; 2) Lactato de cálcio: imersão de 1 minuto antes do tratamento clareador; 3) Fluoreto de sódio: imersão por 1 minuto antes do tratamento clareador; 4) Lactato de cálcio + fluoreto de sódio: 1 minuto de imersão em solução de lactato de cálcio, seguido de 1 minuto de imersão em fluoreto de sódio antes do tratamento clareador. Os discos de dentina receberam os mesmos protocolos de tratamento (n = 10) para avaliar a permeabilidade. As avaliações da microdureza Knoop e da permeabilidade dentinária foram realizadas duas vezes (no início do estudo e 48 horas após o término do tratamento clareador). Resultados: O modelo linear generalizado considerando o delineamento de medidas repetidas ao longo do tempo mostrou que não houve diferença significativa entre os tratamentos (p = 0,9577) e entre as avaliações (p = 0,3267) em relação à microdureza Knoop. Os testes de Kruskal Wallis e Dunn mostraram que a imersão de lactato de cálcio antes do tratamento clareador proporcionou maior permeabilidade dentinária do que os outros grupos (p = 0,0009). Conclusão: O uso de fluoreto de sódio e lactato de cálcio associado ao clareamento em consultório não influenciou a microdureza do esmalte dentário, embora o lactato de cálcio possa aumentar a permeabilidade dentinária (AU)

O método de fotopolimerização é capaz de influenciar nos valores de microdureza das resinas compostas? Um estudo in vitro / Is the photopolimerization method able to influence on the microhardness values of composite resins? An in vitro study

Introdução: a inovação dos métodos de fotopolimerização foi proposta na tentativa de diminuir o estresse de contração de polimerização das resinas compostas e proporcionar maior conforto ao paciente, reduzindo o tempo de atendimento odontológico. Objetivo: avaliar a microdureza de duas resinas compostas nanoparticuladas submetidas a diferentes técnicas de polimerização. Material e método: quarenta espécimes foram divididos em quatro grupos (n=10) da seguinte forma: Filtek Z350 XT® + técnica imediata (GI); Filtek One Bulkfill® + técnica imediata (GII); Filtek Z350 XT® + técnica de pulso tardio (GIII); Filtek One Bulkfill® + técnica de pulso tardio (GIV). Após o armazenamento em água destilada à temperatura ambiente, os corpos de prova foram direcionados para a medição de microdureza. Utilizou-se teste T para comparação de técnicas e teste Two-Way ANOVA para calcular os efeitos das resinas compostas, técnicas de polimerização e interações referentes à variável dependente (p ≤0,05). Resultado: a resina Filtek Z350 XT® apresentou maior dureza na técnica imediata (GI - 312,45 ± 64,37) e pulso tardio (GIII - 244,50 ± 75,63) comparado à resina Filtek One Bulkfill®, em ambas as técnicas. Observaram-se maiores valores de dureza referentes à técnica imediata, com diferença estatística significativa em relação à resina testada (p = 0,04 - Filtek Z350 XT®; p = 0,03 - Filtek One Bulkfill®). Ambos os fatores isolados (resina e técnicas) apresentaram efeito nos valores de microdureza (p = 0,02 e p < 0,01, respectivamente). Conclusão: a técnica convencional demonstrou atingir maiores valores de dureza quando comparada à técnica de polimerização alternativa.

Introduction: the innovation of photopolymerization methods was proposed in an attempt to reduce the polymerization shrinkage stress of composite resins and also provide more comfort to patient reducing the chair time. The aim of this in vitro study was to assess the microhardness of two nanofilled composite resins subject to different curing techniques. Objective: assess the microhardness of two nanofilled composite resins subject to different curing techniques. Material and method: forty specimens were divided into four groups (N=10) as follows: Filtek Z350 XT® + immediate technique (GI); Filtek One Bulkfill® + immediate technique (GII); Filtek Z350 XT® + delayed pulse technique (GIII); Filtek One Bulkfill® + delayed pulse technique (GIV). After storage in distilled water at room temperature the specimens were assessed for microhardness measurement. T-test was used for comparison of techniques and two-way ANOVA used to calculate the effects of composite resins, curing techniques and their interactions on dependent variable (p set at 0.05). Result: Filtek Z350 XT® resin presented greater hardness on immediate technique (GI - 312,45 ± 64.37) and delayed pulse (GIII - 244,50 ± 75.63) compared to Filtek One Bulkfill® under both techniques. Overall, it was observed greater hardness values under immediate technique with a significant statistical difference apart of tested resin (p = 0.04 - Filtek Z350 XT®; p = 0.03 - Filtek One Bulkfill®). Both isolated factors (resin and techniques) presented effect on microhardness values (p = 0.02 and p < 0.01, respectively). Conclusion: the conventional technique demonstrated to reach higher hardness values when compared to the alternative polymerization technique

Influence of Using Different Light Curing Devices on the Microhardness of a Bulk-Fill Resin / Influência da Utilização de Diferentes Aparelhos Fotopolimerizadores na Microdureza de uma Resina Bulk Fill

Bulk Fill resins are a class of resin composites widely used today and have low polymerization shrinkage. However, these materials need an appropriate light curing technique to have good physical and mechanical properties. The objective of this study was to evaluate the surface microhardness of Bulk Fill resins after their light-curing with two types of high- power light curing devices, using three techniques. 30 specimens were made with a nanoparticulate composite resin Opus Bulk Fill (FGM) and were divided into three groups according to the device and intensity of light curing: Group 1 - light curing with the Emitter B device (Schuster); Group 2 - light curing with the Valo device (Ultradent) at Standard power; and Group 3 - light curing with the Valo device at high power. Higher values of top surface microhardness were observed in Group 3 (microhardness = 53.6 µm), followed by Group 2 (microhardness = 52.1 µm) and Group 1 (microhardness = 33.1 µm), with p values <0.05. Therefore, the Valo light curing unit, in the two powers used, provided greater surface microhardness for the studied specimens. (AU)

Resinas Bulk Fill são uma classe de compósitos resinosos bastante utilizados atualmente e apresentam baixa contração de polimerização. Entretanto, esses materiais necessitam de uma adequada técnica de fotopolimerização para que apresentem boas propriedades físicas e mecânicas. O objetivo deste estudo foi avaliar a microdureza superficial de resinas Bulk Fill fotopolimerizadas com dois tipos de aparelhos fotopolimerizadores de alta potência, em três técnicas de utilização. Foram confeccionados 30 corpos de prova com uma resina composta nanoparticulada Opus Bulk Fill (FGM) e divididos em três grupos de acordo com o aparelho e intensidade de fotopolimerização: Grupo 1 ­ fotopolimerização com o aparelho Emitter B. (Schuster), Grupo 2 ­ fotopolimerização com o aparelho Valo (Ultradent) na potência Standard, Grupo 3 ­ fotopolimerização com o aparelho Valo em alta potência, posteriormente foi realizado o teste de microdureza de Vickers na região superficial de topo dos corpos de prova. Observou-se maiores valores de microdureza superficial de topo no Grupo 3 (microdureza= 53,6 µm), seguido pelo Grupo 2 (microdureza= 52,1 µm) e Grupo 1 (microdureza= 33,1 µm), com valores de p<0,05. Assim sendo, o aparelho fotopolimerizador Valo, nas duas potências utilizadas, forneceu maior microdureza superficial para os corpos de prova estudados. (AU)

Silver Diamine Fluoride versus Bioactive Giomer Light-Curing Varnish: An In Vitro Study on Caries Arrest

ABSTRACT Objective To compare the capacity of silver diamine fluoride (30%) and the bioactive giomer light-curing varnish for arresting ICDAS score 5 non-retentive caries lesions. Material and Methods An in vitro analytical study was conducted using 36 healthy primary teeth, in which a cavity was created, divided into 3 groups: control (distilled and deionized water), giomer-based light-curing varnish - Barrier Coat, and Silver Diamine Fluoride 30% - Cariestop (SDF). The samples were analyzed for mineral loss as measured by surface microhardness (SMH).The Knoop microhardness test was performed using the HVS-1000 microhardness tester. The data were compared by two-way analysis of variance - treatment and time (before and after treatment) followed by Tukey's post-test. The significance level adopted in all analyzes was 5%. Results The specimens treated with giomer showed higher SMH compared to the untreated group but were similar to those of the SDF group. The SDF group, on the other hand, showed no statistically significant difference from the control group (p=0.010). Conclusion The giomer varnish had a remineralizing effect on artificial dentinal caries.

Effect of irrigation protocols on root canal wall after post preparation: a micro-CT and microhardness study

Abstract: The aim of this study was to investigate the effects of different post space irrigation protocols for removing residual filling material from dentin walls, by using microcomputed tomography (micro-CT), and the influence of these protocols on dentin microhardness. Bovine incisors (n = 35) were filled with the single-cone technique and MTA Fillapex (Angelus, Londrina, PR, Brazil). Post space preparation (PSP) was performed 7 days after filling, using the Odous Touch electrical system (Odous De Deus Ind. e Com., Belo Horizonte, MG, Brazil), followed by post space irrigation using manual irrigation, passive ultrasonic irrigation, or Easy Clean, together with 2.5% sodium hypochlorite (NaOCl), or with 2.5% NaOCl and 17% EDTA (NaOCl/EDTA). Micro-CT scans were performed at three time points. The residual filling material was evaluated at three levels: cervical, middle and apical. The Knoop test was measured with four indentations around the canal lumen at three dentin depths: X (100 μm), Y (200 μm) and Z (400 μm). Statistical analysis was performed using ANOVA (p < 0.05). The effects of the activation method (p < 0.001), and the root level (p = 0.013), as well as the interaction between the irrigant and the activation method (p = 0.041), led to different percentages of residual filling material. Lower amounts of residual filling material were observed at the cervical versus the middle and apical levels (p < 0.05). No significant differences were observed in dentin microhardness (p > 0.05). The best removal of the residual filling material was performed using the Easy Clean tip and NaOCl/EDTA, regardless of the activation methods.

Initial Mechanical Stabilization of Conventional Glass Ionomer Cements with Different Active Principles

ABSTRACT Objective: To determine the initial mechanical stabilization of conventional glass ionomer cements (GICs) indicated for the atraumatic restorative treatment (ART) in different storage periods. Material and Methods: Specimens were divided according to the GIC (n=12): IZ - Ion-Z, KM - Ketac Molar Easymix, RS - Riva Self Cure, and GL - Gold Label 9. They were prepared and stored in distilled water. Superficial microhardness (SMH) was evaluated (KHN) in three phases: (A) after 1, (B) 3, and (C) 7 days of storage. Data were submitted to 2-way ANOVA and Tukey tests (α = 5%). Results: The average KHN values for phases A, B, and C were, respectively, 33.05 ± 9.74; 33.21 ± 10.31 and 52.07 ± 11.75 (IZ); 50.35 ± 11.39; 66.05 ± 10.48 and 67.77 ± 13.80 (KM); 89.63 ± 15.59; 71.31 ± 23.86 and 57.70 ± 16.89 (RS); 42.18 ± 9.03; 68.54 ± 6.83 and 57.95 ± 8.24 (GL). Significant differences were observed: GIC, time, and interaction of both (p<0.05). KHN values differed between the groups, except in the GIC parameter for KM and GL. The time parameter values of phase A were lower than those of B and C, except for IZ and RS. Conclusion: The initial mechanical stabilization differed between the types of GIC tested and the storage time, and after the final period, all had similar SMH.

A influência do eugenol na microdureza de duas resinas compostas comerciais / The influence of eugenol on the microhardness of two commercial composite resins

Objetivo: avaliar, in vitro, a dureza superficial e profunda de dois tipos diferentes de resina composta, quandoem contato com o cimento de óxido de zinco e eugenol (IRM®). Métodos: foram selecionadas as resinasCharisma® e Vittra® e confeccionados 80 corpos de prova, sendo 40 para cada marca de compósito, queforam divididos em oito grupos (n=10) conforme o contato (imediato, 7 dias, 14 dias) ou não (grupo controle)com o eugenol. Colocou-se num pote dappen uma porção de IRM e um espécime de resina pronto, que,após a presa do material restaurador temporário e a remoção do exemplar colocado, gerou o molde pararealização das amostras em contato com o eugenol, sendo armazenado em água em temperatura ambiente,para os subgrupos 7 e 14 dias. Em sequência, foi inserido um único incremento de resina composta e polimerizadopor 40 segundos, gerando os espécimes que foram armazenados em local seco para serem submetidosao teste de microdureza Vickers sob uma carga de 300 gramas, com tempo de penetração de 10 segundos.Os dados obtidos foram analisados pelo teste ANOVA, a um nível de significância de p<0,05. Resultados:somente o grupo da resina Charisma® que teve contato imediato com eugenol não atingiu 80% de durezaprofunda em relação à superficial. Entretanto, para todos os grupos analisados, tanto a dureza superficialquanto a profunda aumentaram após o contato com o eugenol em relação ao grupo controle. Conclusão: oeugenol não influenciou negativamente a dureza das resinas compostas.(AU)

Objective: to evaluate, in vitro, the superficial and deep hardness of two different types of composite resin when in contact with zinc oxide eugenol cement (IRM). Method: Charisma® and Vittra® resins were selected and 80 specimens were made, 40 for each composite brand that were divided into eight groups (n = 10) according to contact (immediate, 7 days, 14 days) or no (control group) with eugenol. A portion of IRM and a ready-made resin specimen were placed in a dappen pot, which after setting the temporary restorative material and removing the placed specimen, generated the template for making the samples in contact with eugenol, being stored in water in room temperature for subgroups 7 and 14 days. In sequence, a single increment of composite was inserted and polymerized resin for 40 seconds, generating specimens that were stored in a dry place to be submitted to the Vickers microhardness test under a load of 300 grams, with a penetration time of 10 seconds. The data obtained were analyzed by the ANOVA test, at a significance level of p <0.05. Results: only the Charisma® resin group that had immediate contact with eugenol did not reach 80% deep hardness in relation to superficial hardness. However, for all groups analyzed, both superficial and deep hardness increased after contact with eugenol compared to the control group. Conclusion: eugenol did not negatively influence the hardness of composite resins.(AU)

Efeito de diferentes protocolos fotoativadores e espessura dos incrementos na dureza de resinas Bulk fill / Effect of lightcure protocols and increment thickness in the hardness of Bulk fill composites

As resinas Bulk fill surgiram com o intuito de facilitar a restauração de cavidades profundas. A fotoativação adequada é extremamente importante para que a resina bulk fill ofereça propriedades mecânicas satisfatórias e, longevidade na restauração. Este estudo avaliou a influência da espessura do incremento na microdureza Knoop (KHN) de três resinas bulk fill (n = 5). Cinquenta amostras foram divididas de acordo com o material (Filtek Z250, Filtek One Bulk Fill e Filtek Bulk Fill Flow), espessura (2mm e 4 mm) e tempo de fotoativação (20 e 40s) - Z2502mm20s, Z2502mm40s, One2mm20s, One2mm40s, One4mm20s, One4mm40s, Flow2mm20s, Flow2mm40s, Flow4mm20s e Flow4mm40s. As análises KHN foram realizadas no topo e na base de cada amostra. Os dados foram submetidos à ANOVA a 1 critério e ao Teste de Tukey (p< 0,05). A média e desvio padrão (+/-) dos seguintes grupos foram (Z2502mm20s) 0,85 (+/- 0,01); (Z2502mm40s) 0,92 (+/- 0,01); (One2mm20s) 1,05 (+/- 0,08); (One2mm40s) 0,95 (+/- 0,04); (One4mm20s) 0,93 (+/- 0,04); (One4mm40s) 0,97 (+/ - 0,04); (Flow2mm20s) 0,92 (+/- 0,05); (Flow2mm40s) 0,89 (+/- 0,04); (Flow4mm20s) 0,79 (+/- 0,04) e (Flow4mm40s) 0,90 (+/- 0,03). Os grupos da Filtek One Bulk apresentaram um valor significativamente maior, demonstrando uma polimerização suficiente mesmo na base de incrementos com 4 mm. Concluiu-se que o aumento na espessura do incremento de resinas bulk fill não afetou negativamente a fotoativação(AU)

Bulk fill composites emerged, allowing the restoration of deep cavities easily. Appropriate lightcuring is crucial to bulk fill composite presents satisfactory mechanical properties and restoration longevity. This study evaluated the influence of thickness increment on Knoop microhardness (KHN) of three dental bulk fill composites (n=5). Fifty samples were divided according to composite (Filtek Z250, Filtek One Bulk Fill and Filtek Bulk Fill Flow), thickness (2mm and 4 mm) and time lightcuring (20 and 40 s) - Z2502mm20s, Z2502mm40s, One2mm20s, One2mm40s, One4mm20s, One4mm40s, Flow2mm20s, Flow2mm40s, Flow4mm20s e Flow4mm40s. KHN analysis were performed on the top and the base of each specimen. Data were subjected to one-way ANOVA and Tukey test (p< 0,05). The mean and standard deviation (+/-) of following groups were (Z2502mm20s) 0,85(+/-0,01); (Z2502mm40s) 0,92(+/- 0,01); (One2mm20s) 1,05(+/-0,08); (One2mm40s) 0,95(+/-0,04); (One4mm20s) 0,93 (+/-0,04); (One4mm40s) 0,97(+/-0,04); (Flow2mm20s) 0,92(+/- 0,05); (Flow2mm40s) 0,89(+/-0,04); (Flow4mm20s) 0,79(+/-0,04) e (Flow4mm40s) 0,90(+/-0,03) Filtek One Bulk groups present significantly higher value, demonstrating sufficient polymerization even on the base of 4 mm increments. It was concluded that the increase in the thickness increment of Bulk fill composites did not negatively affect the lightcure(AU)

Avaliação in vitro da microdureza e porosidade de duas resinas compostas fotopolimerizáveis / Evaluación in vitro de la microdureza y porosidad de dos resinas compuestas fotopolimerizables / In vitro evaluation of the microhardness and porosity of two photopolymerizable composite resins

RESUMO Introdução: Os estudos científicos acerca das propriedades físicas e mecânicas apresentadas pelas resinas compostas são cada vez mais necessários diante da grande variedade de produtos disponíveis no mercado atual, resultante do aumento de sua demanda dentro da odontologia que preza por preparos minimamente invasivos com a devolução das características estéticas e funcionais do elemento dentário. Objetivo: Avaliar e comparar a microdureza e porosidade das resinas compostas fotopolimerizavéis Filtek Z350 XT 3M e Zirconfill Technew. Métodos: Foram confeccionados 10 corpos de prova por amostra (n= 10) submetidos a teste microdureza Vickers e porosidade por microtomografia computadorizada. Resultados: Com relação à presença de porosidades, dada em porcentagem, o grupo da Filtek apresentou os menores valores médios. Quando comparado estatisticamente, os grupos apresentaram diferença estatística (p= 0,019), com uma magnitude de efeito alta. Com relação aos valores de microdureza, o grupo da Filtek apresentou os maiores valores médios. Quando comparados estatisticamente, os grupos não apresentaram diferença estatística (p > 0,05). Conclusões: A porosidade foi significativamente diferente entre os grupos estudados, sendo o grupo Filtek Z350XT de menor percentual. No entanto, os grupos não apresentaram diferença estatística para microdureza, apesar do grupo Filtek Z350XT ter apresentado maior valor médio(AU)

RESUMEN Introducción: Los estudios científicos sobre las propiedades físicas y mecánicas presentadas por las resinas compuestas son cada vez más necesarios ante la gran variedad de productos disponibles en el mercado actual, resultante del aumento de su demanda dentro de la odontología que aprecia por preparaciones mínimamente invasivas con la devolución de las características estéticas y funcionales del elemento dental. Objetivo: Evaluar y comparar la microdureza y porosidad de las resinas compuestas fotopolimerizables Filtek Z350 XT 3M y Zirconfill Technew. Métodos: Se han confeccionado 10 cuerpos de prueba por muestra (n= 10) sometidos a prueba de microdureza Vickers y porosidad por microtomografía computarizada. Resultados: Con respecto a la presencia de porosidades, dada en porcentaje, el grupo de Filtek presentó los menores valores medios. Cuando se comparó estadísticamente, los grupos presentaron una diferencia estadística (p= 0,019), con una magnitud de efecto alto. Con respecto a los valores de microdureza, el grupo de Filtek presentó los mayores valores medios. Cuando se comparó estadísticamente, los grupos no presentaron una diferencia estadística (p> 0,05). Conclusiones: La porosidad fue significativamente diferente entre los grupos estudiados, siendo el grupo Filtek Z350XT de menor porcentaje. Sin embargo, los grupos no presentaron diferencia estadística para microdureza, a pesar de que el grupo Filtek Z350XT presentó un valor medio más alto(AU)

ABSTRACT Introduction: Scientific studies about the physical and mechanical properties of composite resins are increasingly needed in view of the wide variety of products available in the market today, resulting from the increase in their demand for dental care purposes, with a preference for minimally invasive preparations aimed at restoring the esthetic and functional characteristics of the treated element. Objective: Evaluate and compare the microhardness and porosity of the photopolymerizable composite resins Filtek Z350 XT and Zirconfill Technew. Methods: Ten test bodies were developed per sample (n= 10) and subjected to Vickers microhardness and porosity testing by computerized microtomography. Results: With respect to the presence of porosity, expressed in percentages, the Filtek group had the lowest mean values. When compared statistically, the two groups showed a statistical difference (p= 0.019) with a high effect magnitude. Regarding microhardness, the Filtek group had the highest mean values. Statistical comparison did not find any difference between the groups (p> 0.05). Conclusions: Porosity was significantly different in the groups studied, the Filtek Z350XT group exhibiting the lowest percentage. However, the groups did not show any statistical difference concerning microhardness, despite the fact that the Filtek Z350XT group had a higher mean value(AU)

Dental bleaching gels do not alter the surface roughness and microhardness of feldspathic porcelain / A rugosidade e a microdureza da superfície de porcelana feldspática não são alteradas pelo clareamento dental

ABSTRACT Objective: To evaluate whether two different bleaching gels affect the microhardness and surface roughness of feldspathic ceramic specimens, in vitro. Methods: A total of 48 feldspathic porcelain IPS In Line (Ivoclar-Vivadent) discs (16/treatment group) were immersed in distilled water (Group I, Untreated control, UN), or treated with the bleaching gels: Opalescence (15% carbamide peroxide; OPA) and Opalescence Xtra Boost (38%hydrogen peroxide; OPAXB), for 1h or 6h daily for 14 days. Surface roughness (Ra) and microhardness (Knoop, or KNP) measurements were made before and after treatment, and data were subjected to statistical analysis by paired Student's t-test (p < 0.05). Results: Treatments using Opalescence and Opalescence Xtra Boost did not altered surface roughness (p=0.6199861) or microhardness (p=0.14286744) of the feldspathic porcelain tested in this study. Conclusion: Bleaching treatments using Opalescence and Opalescence Xtra Boost may be suitable for treatment in patients having ceramic prosthodontic treatment. Conclusion: Bleaching treatments using Opalescence and Opalescence Xtra Boost may be suitable for treatment in patients having ceramic prosthodontic treatment.

RESUMO Objetivo Avaliar se dois géis clareadores diferentes afetam a microdureza e a rugosidade superficial de corpos de prova de cerâmicafeldspática, in vitro. Métodos um total de 48 discos de porcelana feldspática IPS In Line (Ivoclar-Vivadent) (16 / grupo de tratamento) foram imersos em água destilada (Grupo I, Controle não tratado, ONU), ou tratados com os géis clareadores: Opalescence (15 % peróxido de carbamida; OPA) e Opalescence Xtra Boost (38% peróxido de hidrogênio; OPAXB), por 1h ou 6h diariamente por 14 dias. Medidas de rugosidade superficial (Ra) e microdureza (Knoop, ou KNP) foram regristradas antes e depois do tratamento, e os dados foram submetidos à análise estatística por teste t de Student pareado (P <0,05). Resultados Os tratamentos com Opalescence e Opalescence Xtra Boost não alteraram a rugosidade superficial (p = 0,6199861) ou a microdureza (p = 0,14286744) da porcelana feldspática testada neste estudo. Conclusão Os tratamentos clareadores com Opalescence e Opalescence Xtra Boost podem ser adequados para o tratamento de pacientes submetidos ao tratamento com prótese cerâmica.

Effect of CPP-ACP on remineralization of artificial caries-like lesion: an in situ study

Abstract The purpose of this double-blind, randomized, crossover in situ study is to compare remineralization of preformed enamel lesions by casein phosphopeptide-stabilized amorphous calcium phosphate (CPP-ACP) and fluoride dentifrice products. During each of four 10-day experimental legs, 10 participants wore intraoral removable palatal acrylic appliances with four human enamel slabs with preformed lesions. A 0.03-mL treatment paste was dripped extraorally onto the enamel blocks once a day for 3 min. The four randomly allocated treatments were as follows: CO- Control: silica dentifrice without fluoride; MP: MI Paste; MPP: MI Paste Plus and FD: Fluoride dentifrice - 1100 ppm F as NaF). Knoop surface hardness (SH) test was performed in three stages (T0 - sound enamel, T1 - after preformed lesion, and T2 - after treatment) and the cross-sectional hardness (CSH) test was performed after treatment using a 50-gram Knoop load for 15 s. Knoop hardness number (KHN) was similar between treatments. %SHr was significantly higher in the MP, FD, and MPP when compared to CO group (Kruskal-Wallis and Mann-Whitney tests, p < 0.05). Harder enamel was found in MP (75 μm) and FD groups at 75 to 175 μm. Treatment with DF, MP, and MPP promoted an increase of 20.27%, 19.24%, and 14.71%, respectively, in Integral Hardness Change (ΔIHC) when compared to CO (p<0.05). Remineralizing agents (MP, MPP, and DF) were able to inhibit demineralization of human enamel subjected to high cariogenic challenge in situ. DF had the greatest preventive potential against the progression of carious lesions.

Effect of the manual manipulation of composite resin with latex gloves / Efecto de la manipulación manual de resina compuesta con guantes de látex

Purpose: This in vitro study aimed to evaluate the influence of the manual manipulation of two composite resins: Filtek™ Z350XT (3M ESPE) and Herculite Précis® (Kerr), with latex gloves contaminated with powder, human saliva and alcohol, on the microhardness values. Material and Methods: Manual manipulation was evaluated using latex gloves with powder, latex gloves without powder, latex gloves without powder with saliva, latex gloves without powder with alcohol, and without hand manipulation or contaminants (control). Each resin was manually manipulated for 10 seconds and photoactivated for 20 seconds with a light intensity of 1000mW/cm2 using a VALO ­Ultradent LED light­ cured unit, and then each sample was evaluated on the microhardness Vickers tester Leitz (Wetzlar). The collected data were analyzed using Kruskal ­Wallis and Mann ­ Whitney post-test (p<0.05). Results. Microhardness values showed a significant difference between the evaluated and control groups, showing lower microhardness values in the group of latex glove with powder for Filtek™ Z350XT and the group of latex glove without powder with saliva for Herculite Précis®. Conclusion. The manual manipulation of composite resins decreases their surface microhardness.

Propósito: Este estudio in vitrotuvo como objetivo evaluar la influencia de la manipulación manual de dos resinas compuestas: Filtek ™ Z350XT (3M ESPE) y Herculite Précis® (Kerr), con guantes de látex contaminados con polvo, saliva humana y alcohol, sobre los valores de microdureza. Material y Métodos: La manipulación manual se evaluó utilizando guantes de látex con polvo, guantes de látex sin polvo, guantes de látex sin polvo con saliva, guantes de látex sin polvo con alcohol, y sin manipulación manual o contaminantes (control). Cada resina fue manipulada manualmente durante 10 segundos y fotoactivada durante 20 segundos con unaintensidad de luz de 1000mW/cm2 usando una unidad de fotocuración LED VALO - Ultradent, y luego cada muestra fue evaluada en el tester de microdureza Vickers Leitz (Wetzlar). Los datos recopilados se analizaron utilizando Kruska ­Wallis y post-test Mann­ Whitney (p<0.05). Resultados: Se observó una diferencia significativa en los valores de microdureza entre los grupos evaluados y el grupo control, con valores más bajos de microdureza en el grupo de guantes de látex con polvo para Filtek™ Z350XT y el grupo de guantes de látex sin polvo con saliva para Herculite Précis®. Conclusión. La manipulación manual de resinas compuestas disminuye su microdureza superficial.

Evaluation of the effect of coating vertex denture lining material with plant oils on microbial growth and hardness

Aims: To evaluate the effect of surface coating with natural plant oils (Salvia officinalis, ginger and eucalyptus) on Candida growth and the hardness of Vertex denture lining material. Materials and method: Forty five specimens were prepared from soft acrylic lining material, twenty five of which were 10x10x2mm in size for testing antifungal activity, and twenty samples were 20mm in diameter and 12mm in thickness, for testing shore A hardness after coating samples with three types of natural oils (Salvia officinalis, ginger and eucalyptus oils). Significant differences among the groups at (p≤0.05) level of significance were determined statistically with one way analysis of variance and Duncan's multiple range test Result: Antifungal assay showed a significant difference between five groups regarding Candida albicans growth (p≤ 0.05). For the hardness test, comparing different times of storage in water (1, 7, 14, 30 days) revealed a significant difference within all groups (p≤0. 05). While comparing the groups coated with natural oils with the control group, significant differences were found between different times of storage in water (1, 7, 30 day) (p≤0.05), except at 14 days of water storage there was no significant difference between groups (p>0.05). Conclusion: All tested natural oils were effective as fungicidal agents and increased the softness and duration of soft acrylic lining material.

The Impact of Radiotherapy in the in Vitro Remineralization of Demineralized Enamel

Objective: To evaluate the impact of radiotherapy on enamel around restorations of glass ionomer cement (GIC) and fluoride tooth paste (FTP). Material and Methods: Eighty enamel blocks were made and randomly distributed into two groups, according to the fluoride therapy, non-fluoride tooth paste (NFTP) and FTP (n=40) and in subgroups in conformity with radiation dose (0, 10, 30 and 60 Gy). Roughness and microhardness enamel analyses were conducted before radiotherapy. Enamel cavities were made and restored with two GIC (Ketac Molar Easy Mix or Vitremer). Enamel blocks were submitted to 10, 30 and 60 Gy. Then, artificial enamel caries lesions were created by a pH-cycling procedure and FTP or NFTP were used as treatment. The restored enamel blocks were submitted to final roughness and microhardness analyses. Roughness increase (ΔR) and hardness loss (ΔH) values of enamel were submitted to ANOVA and Tukey test (p=0.05). Results: The irradiated enamel group showed statistically higher ΔR (0.44 ±0.2) and ΔH (99.26±7.0) values compared to non-irradiated group (ΔR = 0.051±0.02; ΔH=66.16±12.7) when a resin-modified GIC and NFTP were used. Conclusion: Higher radiation dose increased dissolution of bovine enamel. The use of GIC associated with FTP decreased roughness and increased enamel hardness after radiotherapy.

Efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina / The effect of age on morphological, chemical and physical aspects of human and bovine root dentin

Dentes bovinos têm sido utilizados como substitutos aos humanos em pesquisas odontológicas. Entretanto, faltam dados que suportem o uso da dentina radicular bovina, sobretudo, que analisem o efeito da idade nas propriedades do substrato. Assim, analisou-se o efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina, em função dos terços da raiz. Trata-se de um estudo experimental, in vitro, aprovado pelo Comitê de Ética em Pesquisa (COEP-UFMG 1.803.933) e pela Comissão de Ética no Uso de Animais (CEUAUFMG 372/2016). A amostra foi composta por dentes unirradiculares, cujas dentinas radiculares foram categorizadas em: humana jovem (HJ, 20-30 anos); humana madura (HM, acima de 60 anos); bovina jovem (BJ, 24-36 meses); e bovina adulta (BA, acima de 48 meses). Os dentes foram seccionados abaixo da junção amelocementária e ao longo eixo da raiz, para a obtenção de hemisecções. Uma hemisecção foi escolhida e cortes foram feitos para a obtenção dos espécimes, conforme cada método de análise. Para as análises dos aspectos morfológicos ­ número, diâmetro e área dos túbulos dentinários ­ os espécimes foram analisados em Microscópio Eletrônico de Varredura. A composição química foi analisada por Espectroscopia de Raios X por Dispersão em Energia, Espectroscopia por Comprimento de Onda Dispersivo e Espectroscopia Raman por Transformada de Fourier. Na análise das propriedades mecânicas, os espécimes foram submetidos aos testes de nanoindentação, resistência à flexão em três pontos e compressão. Para a análise da resistência ao cisalhamento por extrusão, as raízes receberam tratamento endodôntico e foram fixados pinos de fibra de vidro com cimentos resinosos (dual convencional e autoadesivo). As raízes foram seccionadas nos terços radiculares e os espécimes testados em máquina universal de ensaios. Adicionalmente, avaliou-se o grau de conversão dos cimentos resinosos. Os dados foram analisados em software estatístico, nível de significância de 5%. A HM apresentou os menores valores para número, diâmetro e área de túbulos dentinários (p<0,05). A HM apresentou maiores valores de cálcio, razão Ca/P e concentração mineral relativa, com diminuição na organização e qualidade do colágeno (p<0,05). A HM apresentou os maiores valores de nanodureza, módulo de elasticidade e resistência à compressão, mas os menores valores de resistência à flexão e módulo de elasticidade à flexão (p<0,05). A HM apresentou os menores valores de resistência de união, com diferenças entre os terços radiculares (p<0,05). O grau de conversão dos cimentos apresentou uma diminuição ao longo dos terços radiculares (p<0,05). Concluiu-se que a idade possui um efeito nos aspectos morfológicos, químicos e físicos da dentina radicular humana, sem efeito na dentina bovina. Assim, quando da necessidade de substituição da dentina radicular humana pela bovina em pesquisas, é necessário considerar o efeito da idade nos desfechos analisados.

Bovine teeth have been used as a substitute for human teeth in dental research. However, there is a lack of data that support the use of bovine root dentin, mainly, that analyze the effect of age on the properties of the substrate. Thus, the effect of age on the morphological, chemical and physical aspects of human and bovine root dentin was analyzed, in function of the root thirds. This is an in vitro experimental study, approved by the Research Ethics Committee (protocol number: 1.803.933) and the Ethics Committee on the Use of Animals (protocol number: 372/2016). The sample was composed of single-rooted teeth and root dentin was categorized into: young human (YH, 20-30 years); old human (OH, above 60 years); young bovine (YB, 24-36 months); and adult bovine (AB, over 48 months). The roots were sectioned below the cement-enamel and longitudinally to produce two hemi-sections. One hemi-section was chosen and sections were made to obtain the specimens, according to each method of analysis. For the analyzes of the morphological aspects - number, diameter and area of the dentinal tubules - the specimens were analyzed in Scanning Electron Microscope. The chemical composition was analysed by Energy Dispersive Spectroscopy, Wavelength Dispersive Spectroscopy and Fourier Transformed Raman Spectroscopy. In the analysis of the mechanical properties, the specimens were submitted to nano-indentation, three-point flexural and compression tests. For the analysis of the push-out bond strength test, the roots received endodontic treatment and fiber post with resin cements (conventional and selfadhesive dual) were fixed. The roots were sectioned in the root thirds and the specimens tested in a universal testing machine. Additionally, the degree of conversion of the resin cements was evaluated. The data were analyzed in statistical software, level of significance of 5%. The OH presented the lowest values for number, diameter and area of dentinal tubules (p<0.05). OH showed higher values of calcium, Ca/P ratio and relative mineral concentration, with decrease in the organization and quality of the collagen (p<0.05). The OH showed the highest values of nano-hardness, elastic modulus and compressive strength, but the lowest values of flexural strength and flexural modulus (p<0.05). The OH presented the lowest values of bond strength, with differences among the root thirds (p<0.05). The degree of conversion of the cements showed a decrease along the root thirds (p<0.05). It was concluded that age has an effect on the morphological, chemical and physical aspects of human root dentin, with no effect on bovine dentin. Thus, when it is necessary to replace the human root dentin by the bovine in research, it is necessary to consider the effect of age on the analysed outcomes.

Efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina / The effect of age on morphological, chemical and physical aspects of human and bovine root dentin

Dentes bovinos têm sido utilizados como substitutos aos humanos em pesquisas odontológicas. Entretanto, faltam dados que suportem o uso da dentina radicular bovina, sobretudo, que analisem o efeito da idade nas propriedades do substrato. Assim, analisou-se o efeito da idade nos aspectos morfológicos, químicos e físicos das dentinas radiculares humana e bovina, em função dos terços da raiz. Trata-se de um estudo experimental, in vitro, aprovado pelo Comitê de Ética em Pesquisa (COEP-UFMG 1.803.933) e pela Comissão de Ética no Uso de Animais (CEUAUFMG 372/2016). A amostra foi composta por dentes unirradiculares, cujas dentinas radiculares foram categorizadas em: humana jovem (HJ, 20-30 anos); humana madura (HM, acima de 60 anos); bovina jovem (BJ, 24-36 meses); e bovina adulta (BA, acima de 48 meses). Os dentes foram seccionados abaixo da junção amelocementária e ao longo eixo da raiz, para a obtenção de hemisecções. Uma hemisecção foi escolhida e cortes foram feitos para a obtenção dos espécimes, conforme cada método de análise. Para as análises dos aspectos morfológicos ­ número, diâmetro e área dos túbulos dentinários ­ os espécimes foram analisados em Microscópio Eletrônico de Varredura. A composição química foi analisada por Espectroscopia de Raios X por Dispersão em Energia, Espectroscopia por Comprimento de Onda Dispersivo e Espectroscopia Raman por Transformada de Fourier. Na análise das propriedades mecânicas, os espécimes foram submetidos aos testes de nanoindentação, resistência à flexão em três pontos e compressão. Para a análise da resistência ao cisalhamento por extrusão, as raízes receberam tratamento endodôntico e foram fixados pinos de fibra de vidro com cimentos resinosos (dual convencional e autoadesivo). As raízes foram seccionadas nos terços radiculares e os espécimes testados em máquina universal de ensaios. Adicionalmente, avaliou-se o grau de conversão dos cimentos resinosos. Os dados foram analisados em software estatístico, nível de significância de 5%. A HM apresentou os menores valores para número, diâmetro e área de túbulos dentinários (p<0,05). A HM apresentou maiores valores de cálcio, razão Ca/P e concentração mineral relativa, com diminuição na organização e qualidade do colágeno (p<0,05). A HM apresentou os maiores valores de nanodureza, módulo de elasticidade e resistência à compressão, mas os menores valores de resistência à flexão e módulo de elasticidade à flexão (p<0,05). A HM apresentou os menores valores de resistência de união, com diferenças entre os terços radiculares (p<0,05). O grau de conversão dos cimentos apresentou uma diminuição ao longo dos terços radiculares (p<0,05). Concluiu-se que a idade possui um efeito nos aspectos morfológicos, químicos e físicos da dentina radicular humana, sem efeito na dentina bovina. Assim, quando da necessidade de substituição da dentina radicular humana pela bovina em pesquisas, é necessário considerar o efeito da idade nos desfechos analisados.

Bovine teeth have been used as a substitute for human teeth in dental research. However, there is a lack of data that support the use of bovine root dentin, mainly, that analyze the effect of age on the properties of the substrate. Thus, the effect of age on the morphological, chemical and physical aspects of human and bovine root dentin was analyzed, in function of the root thirds. This is an in vitro experimental study, approved by the Research Ethics Committee (protocol number: 1.803.933) and the Ethics Committee on the Use of Animals (protocol number: 372/2016). The sample was composed of single-rooted teeth and root dentin was categorized into: young human (YH, 20-30 years); old human (OH, above 60 years); young bovine (YB, 24-36 months); and adult bovine (AB, over 48 months). The roots were sectioned below the cement-enamel and longitudinally to produce two hemi-sections. One hemi-section was chosen and sections were made to obtain the specimens, according to each method of analysis. For the analyzes of the morphological aspects - number, diameter and area of the dentinal tubules - the specimens were analyzed in Scanning Electron Microscope. The chemical composition was analysed by Energy Dispersive Spectroscopy, Wavelength Dispersive Spectroscopy and Fourier Transformed Raman Spectroscopy. In the analysis of the mechanical properties, the specimens were submitted to nano-indentation, three-point flexural and compression tests. For the analysis of the push-out bond strength test, the roots received endodontic treatment and fiber post with resin cements (conventional and selfadhesive dual) were fixed. The roots were sectioned in the root thirds and the specimens tested in a universal testing machine. Additionally, the degree of conversion of the resin cements was evaluated. The data were analyzed in statistical software, level of significance of 5%. The OH presented the lowest values for number, diameter and area of dentinal tubules (p<0.05). OH showed higher values of calcium, Ca/P ratio and relative mineral concentration, with decrease in the organization and quality of the collagen (p<0.05). The OH showed the highest values of nano-hardness, elastic modulus and compressive strength, but the lowest values of flexural strength and flexural modulus (p<0.05). The OH presented the lowest values of bond strength, with differences among the root thirds (p<0.05). The degree of conversion of the cements showed a decrease along the root thirds (p<0.05). It was concluded that age has an effect on the morphological, chemical and physical aspects of human root dentin, with no effect on bovine dentin. Thus, when it is necessary to replace the human root dentin by the bovine in research, it is necessary to consider the effect of age on the analysed outcomes.

Micro-hardness distribution of proximal tibia in human skeleton / 中华骨科杂志

Objective@#To investigate the microhardness distribution of cancellous bone in the proximal tibia and its clinical significance.@*Methods@#Three fresh tibias were obtained and examined by X-ray and CT to exclude skeletal pathologies, such as osteoporosis, osteoarthritis. According to the Heim's square, the proximal tibias were cut off. Each of the proximal tibias was divided into three parts, the medial condyle, the intercondylar area and the lateral condyle. Each part was divided into three sections, proximal, middle and distal sections. Each of the proximal tibias was divided into 9 regions. Bone specimens with a thickness of 3 mm were taken from each region using a high precision low-speed saw and fixed on flat sheets. The microhardness of the bone tissue was measured using a Vickers microhardness tester after polish. Ten effective micro-indentation tests were conducted in each region. After measurement the diagonal length of the indentations, the microhardness values were calculated via software provided by the hardness tester. Analysis of variance and Tukey method were used to compare the microhardness values of different parts, sections and regions of cancellous bone. The microhardness distribution of the proximal tibia was analyzed.@*Results@#A total of 270 effective indentations were made in the specimens, and the microhardness values were obtained. The average microhardness of the three proximal tibias was 40.98±3.44, 34.92±4.64 and 39.49±3.86 HV, respectively. There was a significant difference among the groups (F=55.87, P=0.000). The microhardness distribution of bone tissue in the three proximal tibias was similar. In the comparison of different parts, the microhardness of medial condyle was greater than that of the lateral condyle, which was larger than that of the intercondylar area. The difference between the parts was statistically significant (F=18.42, 8.236, 10.877; P=0.000, 0.001, 0.000). In the comparison of different sections, the microhardness of the distal section was greater than that of the proximal section, which was larger than that of the middle section. The difference between the sections was statistically significant (F=8.720, 17.140, 6.142; P=0.000, 0.000, 0.003). The microhardness distribution was similar among different regions. The region with the highest microhardness is the medial condyle of the distal section with microhardness of 44.87±3.25 HV (range 39.2-49.7 HV). The lowest microhardness was in the intercondylar area of the middle section with hardness of 29.41±4.53 HV (range 24.8-36.2 HV).@*Conclusion@#The microhardness value of cancellous bone near the articular surface at the proximal tibia was smaller, which could disperse the load and protect the fragile of articular cartilage. Furthermore, the microhardness of the transition zone is larger. The microhardness value of the cancellous bone in medial tibia condyle is the greatest, which is related to load-bearing.

Efeito de diferentes colutórios sobre a microdureza de resinas compostas fotopolimerizáveis / Effect of different mouthwashes on microhardness of photopolymerizable composite resins

Introdução: Na Odontologia, as resinas são utilizadas como materiais restauradores, para o restabelecimento da estética, da função e da forma dos dentes. Objetivo: Avaliar in vitro a microdureza das resinas Filtek Z350 XT® e Filtek Z250 XT®, submetidas ao contato direto quando expostas a colutórios. Material e método: Dez corpos de prova foram confeccionados em uma matriz de náilon, em dois incrementos, e foram fotoativados por 20 s. A homogeneidade da amostra foi verificada através dos testes Mann-Whitney e Kruskal-Wallis, e uma variância paramétrica foi realizada (ANOVA) para a análise de significância, aplicando-se o teste de Tukey a fim de comparar os resultados (α=5%). Resultado: O maior valor médio foi apresentado pelo grupo G1 (Filtek Z350 XT- água destilada- controle) - 138,22(±21,8) e os menores valores foram do grupo G9 (Filtek Z250 XT- Solução de Camomila) - 87,12(±4,39) e do grupo G10 (Filtek Z250 XT- Solução de Romã) - 99,32(±11,10). A resina Filtek Z350 XT foi superior à resina Filtek Z250 XT (p=0,015). Conclusão: A resina Filtek Z350 XT apresentou melhores resultados quando estes foram comparados aos resultados da Filtek Z250 XT.

Introduction: In dentistry, resins are used as restorative materials for the reconstruction of aesthetics, function and shape of teeth. Aim: To evaluate in vitro the microhardness of Filtek Z350 XT® and Filtek Z250 XT® resins subjected to direct contact when exposed to mouthwashes. Material and method: Ten specimens were prepared in a nylon matrix in two increments and photoactivated for 20s. The homogeneity of the sample was verified through the Mann-Whitney and Kruskal-Wallis tests and a parametric variance was performed (ANOVA), and for Tukey significance analysis (α=5%). Result The highest mean value was presented by group G1 (Filtek Z350 XT- distilled water- control) - 138.22 (±21.8), and the least values ​​were from group G9 (Filtek Z250 XT- Chamomile Solution) - 87.12 (±4.39) and the G10 group (Filtek Z250 XT - Pomegranate solution) - 99.32 (±11.10). Filtek Z350 XT resin was superior to Filtek Z250 XT (p=0.015). Conclusion Filtek Z350 XT resin presented better results than Filtek Z250 XT.